Low Temperature Impact Resistance - Polymaker™ PC-PBT has a high resistance to impact. It also features an excellent low temperature toughness keeping more than 70% of its impact resistance at -30°C.

Heat Resistant - Polymaker™ PC-PBT is an excellent choice for heat resistant applications, offering better heat resistance than a range of other material types and withstanding temperatures up to 140ºC.

Good Chemical Resistance - Polymaker™ PC-PBT is resistant to hydrocarbons, alcohols, organic acids, inorganic aqueous salts, and mild base and acid solutions. This makes them suitable for applications requiring resistance to intermittent contact with many lubricants, solvents, fuels, oils, cleaning agents, and other automotive-type chemicals.

Formulated For 3D Printing - Using Covestro’s Makroblend® family as its base material, Polymaker™ PC-PBT is specifically engineered for 3D printing to combine excellent mechanical properties and printing quality. Makroblend® is widely used in various industries. Enclosure and 100°C heated bed required; a heated chamber is highly recommended.

Uncompromised Quality - Polymakers leading quality control process and rigorous in-house testing ensure reliable printing and consistency across spools and batches.

Next >

Print Settings

- Nozzle Temperature: 260°C – 280°C
- Printing Speed: 30mm/s – 50mm/s
- Bed Temperature: 100°C – 115°C
- Chamber Temperature: 100°C – 110°C
- Bed Surface: Almost any surface with glue
- Cooling Fan: OFF
Note: Based on 0.4 mm nozzle and Simplify 3D v.3.1. Printing conditions may vary with different printers and nozzle diameters.

Mechanical Properties

- Young’s Modulus: 1986 ± 85 (MPa)
- Tensile Strength: 41.8 ± 0.9 (MPa)
- Bending Strength: 64.4 ± 0.3 (MPa)
- Impact Strength: 21.4 ± 3 (kJ/m2)
- Impact Strength (-30°C): 15 ± 3 (kJ/m2)

Thermal Properties

- Glass Transition Temperature: 140°C
- Vicat Softening Temperature: 139°C
- Melting Temperature: 223°C

Notes

Recommended Support Materials: PolyDissolve™ S2

Also: When printing with Polymaker™ PC-PBT it is recommended to use a heated chamber.
It is recommended to anneal the printed part right after the printing process to release the residual internal stress when not using a heated chamber.

Annealing settings: 90°C for 2h

Disclaimer: The typical values presented in Polymakers data sheet are intended for reference and comparison purposes only. Due to the nature of 3D printing they should not be used for design specifications or quality control purposes.