Nylon PA6 CF15 is a high-temperature, black, PA6-based construction material. Filling with 15% carbon fibres increases significantly the mechanical strength of the polyamide the material is based on. The filaments specific quality is the moisture absorption reduced by half and the water absorption time is four times lower than that of the pure PA6. Printing does not require a heated chamber and no deformation occurs. The material is compatible with the HIPS and BVOH support materials. In addition, Nylon PA6 CF15 features a very low linear shrinkage (up to 0.1%), a high deformation temperature (240°C), working temperature (180°C) and low thermal expansion coefficient (0.4 10-5/K).
FeaturesSpecsSupport
Key features
Exceptionally low processing (linear) shrinkage of 0.1 %
High temperature and abrasion resistance
Easy separation of the object from the bed
High mechanical strength
Chemical resistance to lubricants and oils
Wide range of applications
Very robust lamination of layers
High creep resistance, high hardness and rigidity of the printed items
Very wide temperature range for prolonged operation as well as a very high temperature up to 180°C for short-time operation
Applications
Production of gear wheels and racks, sweep-off gears and guide rolls operated in elevated temperatures up to 150°C on a prolonged basis and up to 180°C on a short-time basis
All types of ring and plate seals with an increased chemical and corrosion resistance
Due to the essential content of shredded carbon fibre, it is recommended to use nozzles with diameters exceeding the standard value of 0.4mm.
The presence of carbon fibre may also cause the wear of brass nozzle, thus it is recommended to use stainless steel nozzles for prolonged application of PA6 CF15.
NOTE: 1kg Spool is shown
Product Dimensions: 200 x 200 x 52mm
Next >
This product has no specific warranty. Bilby 3D will honor obligations under Australia Consumer Guarantee regulations if and where they apply to this product
10% Bulk Discount available; Order 10 or more filament at once, Prepay for your order, Phone 1800-847-333 to order. Conditions apply.
Nylon PA6 GK10 is a new, high-temperature PA6-based construction material in the natural colour. Perfect for 3D printing. Filled with glass beads, it is more flexible than the polyamide the material is based on. Its specific quality is a low impact of moisture and temperature on the measurements or electrical properties as compared to PA66. In addition, Nylon PA6 GK10 features a low linear shrinkage (up to 0.3-0.5%) and a relatively high working temperature (160oC).
Buy Now
3DXtech Obsidian PA6+CF Black (Onyx Alternative), 1.75mm, 1kg spool
Equivalent to 800cm³, 1kg Obsidian™ PA6+CF is an excellent drop-in replacement for Markforged Onyx™ and is compatible for use in all Markforged and Raise3D printers with toughed nozzles. Obsidian™ delivers excellent performance, appearance, and a significant cost savings.
Buy Now
Raise3D Industrial PA12 CF PLUS - 1.75mm - Black - 1kg Spool
Raise3D Industrial PA12 CF Filament is a carbon fiber-reinforced composite filament material based on Nylon 12 (Polyamide 12)
Buy Now
3DXtech Obsidian PA6+CF Black (Onyx Alternative), 1.75mm, 2kg spool
equivalent to 1600cm³, 2kg Obsidian™ PA6+CF is an excellent drop-in replacement for Markforged Onyx™ and is compatible for use in all Markforged and Raise3D printers with toughed nozzles. Obsidian™ delivers excellent performance, appearance, and a significant cost savings.
Buy Now
3DXtech Obsidian PA6+GF Red (Onyx Alternative), 1.75mm, 1kg spool
Equivalent to 800cm³, 1kg Obsidian™-GF is a Glass Fiber reinforced PA6 that was formulated to print using stock Onyx™ settings. This is an excellent drop-in replacement for Markforged Onyx™ that offers many much-awaited colors in an engineering-grade material.
Buy Now
Spectrum Nylon, PA6 Carbon Fibre, Black, 1.75mm, 1kg Spool - UNTIL SOLD OUT
High temperature construction material
Nylon PA6 CF15 is a high-temperature, black, PA6-based construction material. Filling with 15% carbon fibres increases significantly the mechanical strength of the polyamide the material is based on.
Buy Now
Spectrum Nylon, PA6 Carbon Fibre, 1.75mm, 500g - UNTIL SOLD OUT
High temperature construction material
Nylon PA6 CF15 is a high-temperature, black, PA6-based construction material. Filling with 15% carbon fibres increases significantly the mechanical strength of the polyamide the material is based on. The filaments specific quality is the moisture absorption reduced by half and the water absorption time is four times lower than that of the pure PA6. Printing does not require a heated chamber and no deformation occurs. The material is compatible with the HIPS and BVOH support materials. In addition, Nylon PA6 CF15 features a very low linear shrinkage (up to 0.1%), a high deformation temperature (240°C), working temperature (180°C) and low thermal expansion coefficient (0.4 10-5/K).
Spectrum Carbon PLA is a modified, PLA-based filament blended with carbon fibers which contributes to a considerably higher rigidity, hardness, and tensile resistance while retaining low shrinkage and very good adhesion to build platforms typical for the pure PLA. The 10% addition of carbon fibre enables you to obtain matte surfaces of printed items, which greatly improves the aesthetic properties of printed items.
All prices are in Australian Dollars and include GST. Standard Postage & Handling with Australia is $12 flat rate, free for orders over $350. Express Post starts at $15
Sydney - Kingsgrove, NSW
Melbourne - Clayton, VIC