HighTemp DL400 is the first Photocentric temperature resistant resin possessing superior properties of both strength and stiffness. It can handle impact, compression, fatigue, high temperatures and moisture without bending or deforming.
FeaturesSpecsSupport
Photocentric’s HighTemp DL400 can be used for quick printing applications with an impressive layer thickness of 350 µm.
Best Used for:
• Hot fluid and gas manifolds
• Moulds and inserts
• Heat resistant housings and fixtures
• Outdoor applications
USPs:
• Temperature resistant (Heat Deflection Temperature of 230 °C)
• Excellent long-lasting performance under heat and stress
• Quick and fast prototyping 350 µm layer
• Simulating the strength and stiffness of glass filled Nylon 6
• Smooth surface finish and ability to print fine details
• Minimal shrinkage
• Tensile Modulus*: 4000 MPa under ASTM D638
• Ultimate Tensile Strength*: 80 MPa under ASTM D638
• Elongation at break*: 4% under ASTM D638
Flexural Properties
• Flexural Strength*: 109 MPa under ASTM D790
• Flexural Modulus*: 3300 MPa under ASTM D790
Impact Properties
• Impact Strength Notched Izod*: 3.1 kJ/m2 under ISO 180
General Properties
• Hardness*: 95 Shore D under ASTM D2240
• Heat Deflection Temperature*: 230 °C under ASTM D648 (0.455 MPa)
• Viscosity: 650 cPs at 25°C Brookfield spindle 3
• Density: 1.10 g/cm3
• Storage: 10 - 50°C
• Colour: Amber
• Biocompatibility Cytotoxicity ISO 10993-5 - Passed
* Post cured for 1hr at 60°C in Cure L2
Product Dimensions: 190 x 140 x 260mm
Next >
Processing Instructions
• To print with Photocentric Liquid Crystal Magna, choose ‘HighTemp DL400’ and the desired layer thickness when preparing your print file in Photocentric Studio
• Heat the resin to 60°C for 5 hours or until the resin is fully liquified in the bottle. Failure to do so prior to printing will result in the resin crystalizing, leading to print failures
• Shake the resin bottle for 2 minutes before pouring into the resin vat
Post Processing
• Parts can be washed in 15 minutes using Photocentric Resin Cleaner or alternatively, in 10 minutes using Photocentric Resin Cleaner 30
• Once washed, rinse with warm water for 2 minutes
• Dry with compressed air to remove any remaining water. Or alternatively, leave to air-dry
• Place the platform into the Photocentric Cure L2 for a minimum of 2 hours at 60°C or until parts are fully cured (4 hours maximum)
• Remove the platform from the Cure L2 and immediately submerge in cold water for thermal shocking. Parts can be removed from the platform with minimal effort
• Draining and cleaning the vat is highly recommended after print job completion as the ambient temperature may drop below 23 °C resin crystallization temperature This product has no specific warranty. Bilby 3D will honor obligations under Australia Consumer Guarantee regulations if and where they apply to this product
Material Safety Data Sheet
Photocentric HighTemp DL401 is a rigid resin designed for moulding applications,
possessing both high stiffness and ductility, and capable of withstanding high temperatures.
Buy Now
Daylight Resin, Magna High Tensile White, 5kg
When strong parts are required, Magna High Tensile is the resin of choice. Capable of producing incredibly detailed parts along with great strength, higher than that of injection moulded Polycarbonate with similar mechanical behaviour. High Tensile Resin enables you to 3D print extremely strong and durable parts while maintaining an incredibly high accuracy.
Buy Now
Daylight Resin - Magna Durable - Black - 5kg
Daylight Magna Durable resin is ideal for 3d printing durable, strong objects that can be bent without breaking.
Buy Now
Daylight Resin, Magna Duramax Black, 5kg
Daylight Magna Duramax 3D printing resin has been created for 3D printing functional parts that are very durable and long-lasting, with high impact strength. Thick objects are stiff but can be made to flex under strain, while returning to their original shape.
Buy Now
Daylight Resin, Magna Draft Resin, Translucent Blue, 5kg
Daylight Magna Draft 3D printing resin is our fastest printing resin yet. Specifically designed to allow for detailed, large parts to printed in shorter times for rapid prototyping or even production. This resin works up to a 350 µm layer height with low curing times, reducing print times dramatically. The end parts manufactured exhibit very high strength comparable to acrylic and polyimide.
Buy Now
Daylight Resin, Durable DL110HTR, Black, 5kg
Incredibly versatile resin Durable DL110H can handle impact, compression, bending and stress fatigue without breaking or deforming.
Buy Now
Daylight Resin, Magna Concept Green, 5kg
Bring your model figurines and other designs to life with the Magna Concept Green resin. Print jewellery prototypes or detailed figurines with high strength, durability, and most importantly high accuracy with finished smooth surfaces.