Fiberon PPS+CF, Black, 1.75mm, 500g
PolyMaker Fiberon PPS + 10% Carbon Fibre filament, 1.75mm diameter.
Fiberon™ PPS-CF10 is a carbon fiber reinforced PPS (Polyphenylene sulfide) filament, with minimal warping during printing and no need for a heated chamber. With exceptional mechanical strength, high heat resistance, chemical resistance, V0 flame retardancy, and moisture insensitivity, its specifically designed for professionals operating in extreme conditions.
Features
Specs
Support
Features
• Extreme Heat Resistance - Featuring a heat deflection temperature of up to 252.5°C after annealing[1], Fiberon PPS-CF10 delivers extreme heat resistance for a wide range of demanding environments.
UL94-V0 Flame Retardance - Ideal for automotive, railway and aerospace applications, Fiberon™ PPS-CF10 displays V0 performance in the UL94 flame retardancy test, benefiting applications where respective material approval is required. Fiberon™ PPS-CF10 can reduce the intensity of a fire or slow/stop the spread of fire due to its self-extinguishing characteristics.
• Chemical Resistance - Fiberon™ PPS-CF10 is developed to withstand the harshest environments, delivering outstanding chemical resistance (insoluble in all solvents below 200°C).
• Excellent stiffness & moisture insensitivity - Compounded with 10% chopped carbon fiber, Fiberon PPS-CF10 offers excellent mechanical strength and stiffness for a wide range of jig, fixture, automotive and manufacturing applications. Fiberon PPS-CF is a moisture insensitive composite filament[2] , ensuring excellent mechanical properties regardless of moisture absorption. This is in comparison to parts produced in nylon-based carbon fiber that absorb moisture from the air, a process which reduces tensile strength and stiffness of carbon fiber nylon parts. With Fiberon PPS-CF10 users can print end-use parts for a wide range of industries without concerns of mechanical performance if the component is exposed to humid or wet applications.
• High Speed Capable - Fiberon™ PPS-CF10 is high speed capable industrial material, enabling printing up to 300mm/s on suitable high speed printers.
Printer Compatibility & Excellent Surface Finish - Unlike other ultra performance polymers that require actively heated and high temperature chamber environments, Fiberon PPS-CF has been developed to print on a wide-range of 3D printers that can reach a 310 - 350°C nozzle temperature.
[1] Fiberon™ PPS-CF10 displays the best mechanical and thermal properties when fully crystallized. The printed part will not reach full crystallization during the printing process, an additional step is required: Annealing. PPS-CF10 can be annealed in the oven at 125°C for 16 hours.
[2] Moisture insensitivity does not describe whether the filament should be kept dry for optimal print quality. This description of moisture insensitivity is in the context of the end-use application where extremely moisture sensitive materials like PA6-CF see a significant reduction in mechanical properties as the part absorbs moisture. With PPS-CF moisture absorption is minimal and doesnt impact the mechanical properties of the part. For best printing results PPS-CF should still be kept dry during printing and storage.
Next >
FIBERON PPS-CF10 PHYSICAL PROPERTIES
Density: 1.29 g/cm3
Melt Index: 26.2 g/10min (300°C, 2.16 kg)
Moisture Sensitivity: Moisture Conditioning (70% RH, 23°C) Equilibrium at 0.225% after 25 days. Moisture absorption curve.
Flame Retardancy UL94 - V0 (1.5mm)
FIBERON PPS-CF 10 THERMAL PROPERTIES
• Glass Transition: 97.7°C, DSC, 10°C/min
• Heat Deflection Temperature: 0.45MPa - 252.5°C, 1.8 MPa - 133 °C, HDT Curve, Test: ISO 75
• Vicat Softening Temperature: 267.5°C, ISO 306, GB/T 1633
FIBERON PPS-CF 10 MECHANICAL PROPERTIES
• Youngs Modulus (X-Y): 5446.7 ± 149.0 MPa, ISO 527, GB/T 1040
• Youngs Modulus (Z): 2790.0 ± 152.6 MPa
• Tensile Strength: (X-Y): 59.4 ± 1.3 MPa, ISO 527, GB/T 1040
• Tensile Strength (Z): 32.0 ± 5.1 MPa
• Bending Strength (X-Y): 94.3 ± 1.9 MPa, ISO 306, GB/T 1633
• Bending Strength (Z): 30.0 ± 5.2 MPa
• Charpy Impact Strength Notched (X-Y): 5.3 ± 0.2 kJ/m2 ISO 179, GB/T 9343
• Charpy Impact Strength Un-notched (X-Y): 11.4 ± 0.7 kJ/m2
Next >
This product has no specific warranty. Bilby 3D will honor obligations under Australia Consumer Guarantee regulations if and where they apply to this product
Related Products:
Buy Now
3DXtech Thermax PPS - 1.75mm - 500g Spool
ThermaX™ PPS [Polyphenylene Sulfide] is widely used in the most demanding applications because it has excellent chemical resistance coupled with superior mechanical and thermal properties.
Buy Now
3DXTech Thermax PPSU Filament - 1.75mm - Natural - 500g
Polyphenylsulfone (PPSF or PPSU) is a high-temperature aromatic sulfone polymer, printing at 360-390°C. Long considered to be one of the highest performance polymers in the plastics world. PPSU has excellent thermal and chemical resistance, making it well suited for demanding applications in automotive, aerospace, electronics, defense, industrial, medical, semi-con applications. Previously only available to Stratasys customers – now you can print with this ultra performance polymer.
Buy Now
Raise3D Industrial PPS + CF with RFID - 1.75mm - Black - 500g
Traditional engineering plastics often struggle to maintain long-term stability in extreme environments such as high temperatures and severe corrosion.