A High Temperature, durable plastic with good mechanical properties - see Specs tab

With a printing Temperature of 250 - 270 °C, check your 3D printer can work reliably at this temperature before ordering

Next > More Information

Recommended Print Settings
- Nozzle Size: 0.4mm
- Nozzle Temperature: 250 - 270 °C
- Bed Temperature: 80 - 105 °C
- Build Surface: BuildTak or similar
- Cooling Fan: Turned off
- Printing Speed: 60 mm/s
- Raft separation distancce: 0.2 mm
- Retraction Distance: 1mm
- Retraction Speed: 20 mm/s
- Recommended Chamber Temperature: 70 - 80 °C
- Overhang Threshold Angle: 60 °
- Recommended Support Material: PolyMaker PolySupport

Physical Properties

Property	Testing Method	typical Value
Density	ASTM D792 (ISO 1183, GB/T 1033)	1.19 – 1.20 (g/cm3 at 21.5°C)
Glass transition temperature	DSC, 10 °C/min	113 °C
Vicat Softening temperature	ASTM D1525 (ISO 306 GB/T 1633)	119 °C
Melt index	260 °C, 1.2 kg	8-11 (g/10 min)
Decomposition temperature	TGA, 20 °C/min	129- 132 °C

mechanical Properties
PropertyTesting Methodtypical Value Young’s modulus (X-Y) ASTM D638 (ISO 527, GB/T 1040) 2307 ± 60 MPa Tensile strength (X-Y) ASTM D638 (ISO 527, GB/T 1040) 62.7 ± 1.3 MPa Elongation at break (X-Y) ASTM D638 (ISO 527, GB/T 1040) 3.2 ± 0.4 % Bending modulusASTM D790 (ISO 178, GB/T 9341) 2477 ± 159 MPa Bending strengthASTM D790 (ISO 178, GB/T 9341) 100.4 ± 2.7 MPa Charpy impact strength ASTM D790 (ISO 178, GB/T 9341) 3.4 ± 0.1 kJ/m2
All testing specimens were printed under the following conditions:
nozzle temperature = 255 °C, printing speed = 60 mm/s, build plate temperature = 100 °C, infill = 100%
All specimens were conditioned at room temperature for 24h prior to testing

Product Dimensions: 200 x 200 x 70mm