Raise 3D Industrial PPA CF - 1.75mm - Black - 1kg Spool
Raise3D Industrial PPA CF is a carbon fiber-reinforced composite filament material based
on PPA (polyphthalamide or high-performance / high-temperature Nylon).
FeaturesSpecsSupport
Raise3D Industrial PPA GF is a carbon fiber-reinforced composite filament material based
on PPA (polyphthalamide or high-performance/high-temperature Nylon). PPA can be
distinguished from aliphatic polyamides (e.g.PA6) by a higher melting point, glass
transition temperatures (Tg), lower moisture absorption, and greater dimensional stability.
The incorporation of short glass fibers further improves upon the properties of PPA
matrix, which makes PPA GF printed parts promising for end-use applications in the
automotive, aerospace, electrical and electronics (E&E) industries.
This filament is compatible with Raise3D Industrial PPA Support Filament.
See Technical Data Sheet (on Support Tab) for full info
Heat Deflection Temperature (°C)
- 113°C ISO75 1.8 MPa
- 188°C ISO75 0.45 MPa
Note:
Abrasion of the brass nozzle happens frequently when printing PPA GF. Using abrasion resistance nozzle,
such as hardened steel and above grade nozzles are highly recommended.
Recommended Print Settings:
• Nozzle temperature: 290-310°C
• Bed temperature: 65-80°C
• Layer height: 0.1-0.25 mm
• Printing speed: 30-120 mm/s
• Cooling fan: OFF
• Drying temperature: 80-100°C for 4 to 6 hours
• After the printing, it is recommended to anneal the model in the oven at 80-100°C for 8 hours and cool
the room temperature naturally
Next >
This product has no specific warranty. Bilby 3D will honor obligations under Australia Consumer Guarantee regulations if and where they apply to this product
10% Bulk Discount available; Order 10 or more filament at once, Prepay for your order, Phone 1800-847-333 to order. Conditions apply.
Raise HyperCore filament concentrates most of the fibres in the centre of the filament to allow higher speed printing, while increasing layer adhesion and giving a great surface finish.
CarbonX™ CF-HTN is an advanced semi-aromatic polyphthalamide (PPA) reinforced with high-modulus carbon fiber. This polymer is widely used for metal replacement applications that must resist high mechanical loads at elevated temperatures and aggressive chemical environments. HTN has traditionally been a go-to material for demanding applications in automotive, aerospace, oil & gas, electrical, electronics, and industrial markets.
Raise3D Industrial PPA GF is a glass fiber-reinforced composite filament material based
on PPA (polyphthalamide or high-performance / High-Temperature Nylon).
Raise3D Industrial PPA GF is a glass fiber-reinforced composite filament material based
on PPA (polyphthalamide or high-performance / High-Temperature Nylon).
Raise3D Industrial PPA (Polyphthalamide) Support Filament is a break-away support
material specially developed for PPA (Polyphthalamide)
Buy Now
Raise3D E2 - Carbon Fibre
The updated Raise3D E2CF has redesigned extruders and sealed filament boxes specially for the latest Carbon Fibre reinforced materials.
It provides the stability and repeatability of the E2 model, with IDEX - Independant Twin Extruders, and adds the durability of Silicon Carbide nozzles for the most abrasive materials
All prices are in Australian Dollars and include GST. Standard Postage & Handling with Australia is $12 flat rate, free for orders over $350. Express Post starts at $15
Sydney - Kingsgrove, NSW
Melbourne - Clayton, VIC